MIL-C-85285 ( MIL-PRF-85285 ) aliphatic, polyester polyurethane coating is a two component chemically cured product that forms a film that is resistant to chemicals, solvents and abrasion. This product has excellent adhesion to most substrates and is recommended for heavy duty industrial applications where a tough, chemical resistant coating is required. This coating is available in a 4:1 mixture for brush, roll and spray applications. It is specially formulated for excellent ultraviolet ray resistance and superior exterior durability.

PROPERTIES:

1. SOLIDS(weight).....................65 - 75%**
2. SOLIDS(volume).....................53 - 57%**
3. VISCOSITY...........................70 - 90 KU
4. GLOSS @ 60 F.......................90%
5. COLOUR.................................Full Range
6. POT LIFE(77 degrees F)..........6 - 8 Hours*
7. TACK FREE...........................2 Hours*
8. RECOAT...............................Overnight*
9. LIGHT SERVICE......................24 Hours*
10. FULL SERVICE.......................7 Days*
11. VOC(maximum)......................420 g/L
    * Higher temperatures will accelerate dry times and decrease pot life, lower temperatures will lengthen cure times and slightly increase pot life. ** Values will vary with colour.

ADVANTAGES:

1. Excellent Exterior Durability.
2. Abrasion Resistant.
3. Chemical Resistant.
4. Meets ASTM Standard Tests.
5. Resistant to Corrosive Fumes
6. Meets Military Specification

SURFACE PREPARATION:
Surface to be coated must be clean, structurally sound and free of all foreign contaminants including dirt, wax, loose paint or grease. Greasy or oily surfaces should be solvent cleaned with care taken not to paint over moist or wet surfaces. The recommended primer is MIL-P-23377E Type 1 Epoxy Polyamide. The use of alkyd based primers under this coating is not advisable.

Old paint in peeling condition must be removed. Sandblasting or wire brushing are the preferred methods. Chalky paint must also be wire brushed for maximum adhesion.

APPLICATION:
MIL-C-85285 Polyurethane Coating can be brushed rolled or sprayed. Mechanically mix each component, then combine at a ratio of 4:1 by volume. Let admixed material stand for 15 minutes before using to allow for chemical induction. If thinning is required, use MIL-T-81772B Type 1 Polyurethane Thinner.

PRECAUTIONS:

• USE WITH ADEQUATE VENTILATION
• AVOID CONTACT WITH SKIN AND EYES
• READ MATERIAL SAFETY DATA SHEETS BEFORE USING
• KEEP OUT OF REACH OF CHILDREN
• FOR INDUSTRIAL USE ONLY

See product information sheet.

MIL-C-83286B isocyanate/polyester polyurethane coating is a two-component chemically cured product that forms a film that is resistant to chemicals, solvent and abrasion. This product has excellent adhesion to most substrates and is recommended for heavy duty industrial applications where a tough, chemical resistant coating is required. This coating is available in a 1;1 mixture for brush, roll and spray applications. It is specially formulated for excellent ultraviolet ray resistance and superior exterior durability.

PROPERTIES:

1. SOLIDS(weight).....................40 - 45%**,*
2. SOLIDS(volume).....................52 - 55%**,*
3. VISCOSITY...........................70 - 90% KU
4. GLOSS @ 60 DEG...................90%
5. COLOUR.................................Full Range
6. POT LIFE(77 degrees F)..........6 - 8 Hours*
7. TACK FREE...........................2 Hours
8. RECOAT...............................1 Hour
9. LIGHT SERVICE......................24 Hours*
10. FULL SERVICE.......................7 Days*
    Higher temperatures will accelerate dry times and decreases pot life, lower temperatures will lengthen sure times and slightly increase pot life. ** Values will vary with colour. *Catalyzed

ADVANTAGES:

1. Excellent Exterior Durability.
2. Abrasion Resistant.
3. Chemical Resistant.
4. Meets ASTM Standard Tests.
5. Resistant to Corrosive Fumes

SURFACE PREPARATION:
Surface to be coated must be clean, structurally sound and free of all foreign contaminants including dirt, wax, loose paint or grease. Greasy or oily surfaces should be solvent cleaned with care taken not to paint over moist or wet surfaces. The recommended primer is MIL-P-23377F Type 1 Epoxy Polyamide. The use of alkyd based primers under this coating is not advisable. Old paint in peeling condition must be removed. Sandblasting or wire brushing are the preferred methods. Chalky paint must also be wire brushed for maximum adhesion.

APPLICATION:
MIL-C-83286 POLYURETHANE Coating can be brushed rolled or sprayed. Mechanically mix each component, then combine at a ratio of 1:1 by volume. Let admixed material stand for 15 to 30 minutes before using to allow for chemical induction. If thinning is required, use MIL-T-81772B Type 1 Polyurethane Thinner.

PRECAUTIONS:

• USE WITH ADEQUATE VENTILATION
• AVOID CONTACT WITH SKIN AND EYES
• READ MATERIAL SAFETY DATA SHEETS BEFORE USING
• KEEP OUT OF REACH OF CHILDREN
• FOR INDUSTRIAL USE ONLY

See product information sheet.

MIL-C-22750 Epoxy Polymide ( MIL-PRF-22750 ) ( MIL-C-22750D ) ( MIL C 22750 ) ( MIL-PRF-22750F ) is a two-component epoxy polyamide coating for spray and brush applications, furnished in a package kit and suitable for use under air pollution regulations. Formulated for the protection against solvents and chemicals on interior and exterior surfaces. Type11 use for low infrared reflective needs.

See product information sheet.

For more information on our aircraft MIL-SPEC coatings, aerospace coatings, and paint finishes, please feel free to contact us.

MIL-C-46168D hi-solids, aliphatic, polyurethane coating is a two-component chemically cured product that forms a film that is resistant to chemicals, solvents and abrasion. This product has excellent adhesion to most substrates and is recommended for heavy duty industrial applications where a tough, chemical resistant coating is required. This coating is available in a 4:1 mixture for brush, roll and spray applications. It is specially formulated for excellent ultraviolet ray resistance and superior durability.

PROPERTIES:

1. SOLIDS(weight).....................65 - 70%**
2. SOLIDS(volume).....................53 - 57%**
3. VISCOSITY...........................70 - 90 KU
4. COLOUR.................................Full Range
5. POT LIFE(77 degrees F)..........6 - 8 Hours*
6. TACK FREE...........................2 Hours*
7. RECOAT...............................Overnight*
8. LIGHT SERVICE......................24 Hours*
9. FULL SERVICE.......................7 Days*
   *Higher temperatures will accelerate dry times and decrease pot life, lower temperatures will lengthen cure times and slightly increase pot life. **Values will vary with colour.

ADVANTAGES:

1. Excellent Exterior Durability.
2. Abrasion Resistant.
3. Chemical Resistant.
4. Meets MIL-C-46168D Specs.
5. Resistant to Corrosive Fumes.

SURFACE PREPARATION:
Surface to be coated must be clean, structurally sound and free of all foreign contaminants including dirt, wax, loose paint or grease. Greasy or oily surfaces should be solvent cleaned with care taken not to paint over moist or wet surfaces. The recommended primer is MIL-P-23377E Type 1 Epoxy Polyamide. The use of alkyd based primers under this coating is not advisable. Old paint in peeling condition must be removed. Sandblasting or wire brushing are the preferred methods. Chalky paint must also be wire brushed for maximum adhesion.

APPLICATION:
MIL-C-46168D HI-SOLIDS Polyurethane Coating can be brushed, rolled or sprayed. Mechanically mix each component, then combine at a ratio of 4:1 by volume. Let admixed material stand for 15 minutes before using to allow for chemical induction. If thinning is required, use MIL-T-81772B Type 1 Polyurethane Thinner.

PRECAUTIONS:

• USE WITH ADEQUATE VENTILATION
• AVOID CONTACT WITH SKIN AND EYES
• READ MATERIAL SAFETY DATA SHEETS BEFORE USING
• KEEP OUT OF REACH OF CHILDREN
• FOR INDUSTRIAL USE ONLY

See product information sheet.

For more information on our aircraft MIL-SPEC coatings, aerospace coatings, and paint finishes, please feel free to contact us.

Single component moisture curing polyurethane

For more information, please feel free to contact us.

An air-dry, silicone enamel conforming to MIL-E-24635B. It is highly weather resistant with excellent colour and gloss retention.

For more information, please feel free to contact us.

A fast dry, low volatile organic compound content, lusterless alkyd enamel formulated to meet Federal Specification MIL-E-11195E. This enamel is lead and chromate free and is for use on primed interior and exterior metal surfaces.

For more information, please feel free to contact us.

MIL-DTL-15090D, Formula 111 is a light gray equipment enamel for use as a topcoat on equipment, furniture and electrical equipment such as switchboard installations. This coating may be used wherever VOC air pollution regulations apply and is an air dry, solvent base topcoat for use in all interior dry areas.

For more information, please feel free to contact us.

A cellulose nitrate lacquer used in both the manufacture of small arms ammunition for identification purpose and in the assembly of small arms ammunition primers.

See product information sheet.

For more information, please feel free to contact us.

A general purpose exterior protective coating that is particularly formulated for resistance to lubricating oil.

For more information, please feel free to contact us.

A nitrocellulose camouflage lacquer for metal surfaces, particularly formulated for resistance to diester lubricating oil, and is primarily intended for spray application.

For more information, please feel free to contact us.

A general purpose, exterior protective acrylic lacquer coating for metal surfaces. This coating is particularly formulated for resistance to diester lubricating oil and heat for the aircraft industry. Available in gloss, semi-gloss and lusterless finishes. Meets MIL-L-81352A for protection of metal surfaces.

PROPERTIES:

1. Colours..................................All 595 Colours
2. Viscosity.(#4 Ford Cup)..........16-22 Seconds
3. Shelf Life.............................1 Year From Date Of Mfg.
4. Dry Hard..............................Within 40 Minutes
5. Resistant To:
   - Heat, Weather, Water, Hydrocarbons, Lubricating Oil

ADVANTAGES:

1. Meets MIL-L-81352A.
2. Weather Resistant.
3. Fast Dry.
4. Full Colour Range, 595 Colours.
5. Durable Exterior Coating

USES:

1. Steel.
2. Machinery.
3. Aircraft.
4. Vehicles.
5. Equipment
6. Towers

APPLICATION AND REDUCTION:
MIL-L-81352A Acrylic Laquers can be applied by conventional or airless spray application. For spraying, thin up to 10% or as needed with TT-T-266 Thinner. For brushing, reduce up to 10% with MIL-T-81772B TY.3 Thinner. Brush small areas only.

SURFACE PREPARATION:
Surface must be clean , dry and free of all contamination before application of primer.

STEEL:
Surface must be clean and free of all oil, grease and foreign material. Badly rusted or pitted steel should be cleaned by commercial sandblasting and primed the same day.

PRECAUTIONS:

• CONTENTS ARE COMBUSTIBLE
• KEEP AWAY FROM HEAT AND OPEN FLAME
• KEEP OUT OF REACH OF CHILDREN
• DO NOT TAKE INTERNALLY
• AVOID BREATHING VAPOUR OR MIST
• DO NOT USE IN TANK OR PIT WITHOUT PROPER PROTECTION
• READ MATERIAL SAFETY DATA SHEET BEFORE USE OF THIS PRODUCT

For more information on our aircraft MIL-SPEC coatings, aerospace coatings, and paint finishes, please feel free to contact us.

A high grade, single component, air dry, high gloss alkyd enamel formulated for interior and exterior primed metal and wood surfaces.

Federal Specification TT-E-490E is canceled. For future procurement, use Military Specification MIL-E-24635A, Silicone Alkyd Copolymer Enamel, (Metric), dated June 19, 1991.

For more information on our aircraft MIL-SPEC coatings, aerospace coatings, and paint finishes, please feel free to contact us.

A quick-dry, lusterless styrenated alkyd enamel formulated to meet Federal Specification TT-E-516A. Its quick-dry characteristics makes it an excellent production enamel for metal surfaces.

For more information on our aircraft MIL-SPEC coatings, aerospace coatings, and paint finishes, please feel free to contact us.

TT-P-529G is a semi-gloss, alkyd enamel formulated for interior and exterior metal and wood surfaces. This coating is primarily used as a medium dry finish coat on equipment.

See product information sheet.

TT-L-20A is a nitrocellulose lacquer used primarily on metal surfaces, usually specified by the Government for camouflage surfaces.

See product information sheet.

A very high quality nitrocellulose lacquer for general interior use as a finishing coat over a primed metal or a sealed wood substrate.

For more information on our aircraft MIL-SPEC coatings, aerospace coatings, and paint finishes, please feel free to contact us.

TT-P-2756A is intended for use on aircraft weapon systems and other applications where metallic and polymeric substrates require protection. It is self priming and low VOC with a maximum of 420 grams/liter content. Mixing ratio is 4:1 by volume.

See product information sheet.

Home
Aircraft Coatings    PPG Aerospace - PRC-DeSoto    PPG Aviation - Desothane    Strippers & Cleaners (Aviation)
Aerosol - Spray Can    Solid Film Lubricants    Automotive Coatings    Spray Equipment
Supplied Air Masks    How To Order    Contact Us

©Copyright Pacific Western Paints Ltd. 2002
Established in 1985, Pacific Western Paints has earned the trust and respect of customers locally and around the globe. We continue to do so by building our reputation by supplying the highest quality paint and spraying products for even the most demanding applications. At Pacific Western Paints, our approach to customer satisfaction makes a difference.

Quality Aircraft MIL-SPEC Coatings, Aerospace Coatings, and Paint Finishes.

Pacific Western Paints Ltd.
#205- 7188 Progress Way, Delta,
B.C., Canada, V4G 1M6

Tel: 604-432-6111 or 604-430-4151
or you can e-mail us at info@pwpaints.com