DC6571-805 is a ready mixed, high heat aluminum coating. It is a silicone coating designed to withstand temperatures of up to 1500degrees F without failure. The pigment used meets Federal Specification TT-P-320, type 1 or 2, class A. There must be metal to metal contact between the substrate and the aluminum pigment for proper adhesion. This coating may be brushed, rolled or sprayed.
PROPERTIES:
- Colours....................Aluminum
- Finish.....................Low Sheen
- Solids(vehicle)...................13 - 15%
- Solids(volume)...................26 - 28%
- Viscosity..........................54 - 67 KU
- Drying Time
To-Touch...............1 hour
Hard Dry...............3 hours
Full Hardness.........400 F @ 1 hour
ADVANTAGES:
- High Heat Resistance.
- Bright Aluminum.
- Durable.
- Meets TT-P-28E.
USES:
- Aerospace Applications.
- Boilers.
- Heat Exchangers.
- Engines.
- Exhausts.
APPLICATIONS:
Apply by brush, roller or spray methods. For brush and roll, thin with Xylene reducer at 10-15% by volume. For spray application, thin with Toluene at 10-15% by volume.
SURFACE PREPARATION:
All surfaces must be cool, dry free of rust, dirt, scale, old paint and any contaminants. There must be metal to metal contact between the substrate and the aluminum pigment in this coating for proper adhesion. A poor preparation of the substrate will result in a poor job.
PRECAUTIONS:
- USE WITH ADEQUATE VENTILATION
- AVOID CONTACT WITH SKIN AND EYES
- READ MATERIAL SAFETY DATA SHEETS BEFORE USING
- DO NOT TAKE INTERNALLY.
- KEEP OUT OF REACH OF CHILDREN
- VAPOUR HARMFUL.
- WASH HANDS AFTER USING.
- FOR INDUSTRIAL USE ONLY
|
A thermosetting resin coating for surfaces of engine components and metal parts. Dyed to semi-transparent blue colour which changes to green upon proper baking.
APPLICATION:
Normally application is dipping or spraying at package viscosity to a dry film thickness of 0.5 to 0.7 mils. If necessary thinning may be done with T-1280 (MIL-T-18362) Thinner not to exceed 5% by volume.
DRY TIME:
After air drying for one hour the coated parts should be baked until the resin coating exhibits a distinct green coloration. Test procedures call for metal panels to be baked at 325deg +/- 5deg. However, the size and shape of the parts may require deviation from this schedule.
VOLUME SOLIDS: 13.3%
PRECAUTIONS:
- USE WITH ADEQUATE VENTILATION
- AVOID CONTACT WITH SKIN AND EYES
- READ MATERIAL SAFETY DATA SHEETS BEFORE USING
- KEEP OUT OF REACH OF CHILDREN
- FOR INDUSTRIAL USE ONLY
|